LL 1209 AA

MFR: 0.9 Density: 0.920 Application: Lamination film

C4-LLDPE-Blown Film(Innovene license)

Petrochemical: Shazand arak

LL1209AA & LL1209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL1209AA & LL1209KJ are suitable for co extrusion blown films with the following advantages: − Improved hot-tack.
− Good optical properties.
− Low gel level and low odour.
− Good substrate adhesion.
− Tough core layer.

Recommended melt temperature for extrusion is about 180°C-225°C.
LL1209AA & LL1209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.

* LL1209AA & LL1209KJ are suitable for food contact.

  • Typical applications for LL1209AA & LL1209KJ are lamination films and heat sealing layers.:

  • Also LL1209KJ is highly recommended for display packaging.:

  • LL1209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns.:

  • Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.:

C4-LLDPE-Blown Film(Innovene license)
Typical properties Test method (DIN) Unit Value
MFI@190°C, 2.16 kg D1238 gr/10min 0.9
Density D2839 gr/ml 0.920
Vicat Softening Point D1525 °C 100
Tensile Strength@Yield, MD/TD D638 Mpa 9.5/9.5
Elongation@Break, MD/TD D638 % 450/800
Tensile Strength@Break, MD/TD D638 Mpa 38/28
Tear Strength, MD/TD D1922 gr/25mic 85/530
Impact Strength, Dart D1709 gr 150
Haze D1003 % 5
Gloss (45°) D2457 Rating 70
Values shown are averages & are not to be considered as product specifications
* 38 microns, 2:1 Blow ratio / MD=Machine Direction, TD=Transverse Direction

LL 1209 AA