LL 0209 AA

MFR: 0.9 Density: 0.920 Application: Liner bags, builders reel, Co-extrusion, shrink silage, green house and mulch film.

C4-LLDPE-Blown Film(Innovene license)

Petrochemical: Shazand arak

LL0209AA & LL0209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer.

In lean blends they offer the following advantages:
− Greater draw down.
− Improved hot-tack and lower seal shrinkage.
− Better tear resistance.
− Higher tensile stress and elongation at break.

LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.

LL0209AA & LL0209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.
Recommended melt temperature for extrusion is about 180°C – 225°C.

* LL0209AA & LL0209KJ are suitable for food contact.

  • LL0209AA & LL0209KJ are suitable for general purpose films, neat or in lean blends with LDPE and other ethylene polymers:

  • Lean blends applications include sacks of all types:

  • FFS and agricultural films:

C4-LLDPE-Blown Film(Innovene license)
Typical properties Test method (DIN) Unit Value
MFI@190°C, 2.16 kg D1238 gr/10min 0.9
Density D2839 gr/ml 0.92
Vicat Softening Point D1525 °C 100
Film *
Tensile Strength@Yield, MD/TD D638 Mpa 10.5/11
Elongation@Break, MD/TD D638 % 620/840
Tensile Strength@Break, MD/TD D638 Mpa 41/32
Tear Strength, MD/TD D1922 gr/25mic 145/370
Impact Strength, Dart D1709 gr 150
Haze D1003 % 10
Gloss (45°) D2457 Rating 56
Values shown are averages & are not to be considered as product specifications
* 38 microns, 2:1 Blow ratio / MD=Machine Direction, TD=Transverse Direction

LL 0209 AA